Structure and electrical properties of Zn-doped BiFeO3 films

BiFe_1−xZn_xO₃ (x = 0, 0.5, 1, 1.5, 2 mol%) (BFZO) films were prepared on ITO/glass substrates by a sol-gel method. The effects of different Zn contents on the structures and electrical properties of the BFZO films were investigated. From X-ray diffraction (XRD), microstructure and X-ray spectroscopy (XPS) results, the BFZO films with a Zn content of 1 mol% showed a better crystal structure and grain development, and the Fe²⁺ and oxygen vacancy concentrations in this sample were the lowest among all the evaluated BFZO films. The P-E hysteresis loop indicated that the BFZO films with 1 mol% Zn had the highest remanent polarization (2Pr), which was 82.4 μC/cm², along with a coercive field (2E_c) of 887 kV/cm at the tested electric field of 857 kV/cm. The BFZO film with 1 mol% Zn had the lowest leakage current density, which was 3.54 × 10⁻⁷ A/cm² at the tested electric field of 200 kV/cm. Both at high and low electric fields, the space charge-limited current (SCLC) conduction mechanism was the main leakage mechanism. When the test frequency was 10⁵ Hz, the dielectric constant was 133, and the dissipation factor was 0.015.     

C8 BTBT薄膜结晶形貌及OTFT器件性能研究

以p型共轭有机小分子2,7二辛基[1]苯并噻吩并[3,2‐b]苯并噻吩(C8‐BTBT)作为底栅顶接触有机薄膜晶体管(OTFT)的有源层,采用浸渍提拉法、喷墨打印法和真空蒸镀法三种制备工艺,探究半导体薄膜载流子迁移率与结晶形貌的关系,发现不同工艺下有机小分子呈现出不同的生长行为和结晶情况,在很大程度上决定了OTFT器件性能的优劣;此外,通过XRD分析研究了退火处理对C8‐BTBT结晶的影响。结果表明,真空蒸镀制备的薄膜具有更高的结晶度、衬底覆盖率高,并且呈现出SK(Stranski‐Krastanov)模式的结晶生长特征,相应器件中陷阱密度最低,迁移率高达5.44 cm^2·V^-1·s^-1,开关比超过106;且退火处理会严重破坏C8‐BTBT薄膜的结晶。因此,控制半导体层的生长行为,提升半导体层的覆盖率和结晶度是制备高性能共轭小分子OTFT器件的有效途径。     

2.5 GHz城市环境电磁态势的计算与补偿

复杂城市空间的电磁态势分布可以通过电磁场数值计算的方法进行预测。文章使用矩量法(MOM)结合一致性几何绕射理论(UTD)的方法对2.5 GHz频率下某小区环境中的电磁态势进行了仿真计算以及实际测量。场景中的树木结构在此频率下显示出比较强烈的波动性,对电磁仿真计算结果产生了不可忽略的影响,文中将其对仿真计算结果的影响进行了单独建模仿真,给出其产生影响的经验值,对仿真结果进行修正。修正结果与测量结果对比证明该经验值在该频率下可以有效补偿计算结果的缺失。     

短程反硝化耦合厌氧氨氧化工艺及其应用前景研究进展

短程反硝化以其碳源消耗量、废污泥产量、温室气体排量极低及无需曝气等优势，被认为是最具研究潜势的厌氧氨氧化底物供给技术，成为近年来研究热点。本文首先介绍了短程反硝化工艺原理；其次从污泥源、反应时间、碳源类型、碳源量及pH等5个方面总结了影响短程反硝化工艺启动因素；随后综述了短程反硝化耦合厌氧氨氧化工艺的重要研究进展，同时指出了耦合工艺实验研究与工程应用的不足，并提出了解决实验与工程应用缺陷的方案；最后展望了耦合工艺处理城市污水和工业硝酸盐废水的可行性及应用前景，认为全面分析工业硝酸盐废水化学组分与基于分子生物学水平的宏基因组学测序、元转录组学技术是未来耦合工艺同步处理城市污水和工业硝酸盐废水的研究重点。     

滨海基岩矿床安全开采合理隔离层厚度的确定

针对滨海基岩矿床安全开采合理隔离层厚度留设问题，基于材料力学、结构力学等共七种理论计算方法综合确定隔离层厚度，利用点柱式上向水平分层充填法建立三维数值计算模型，通过结合FLAC3D数值模拟软件，分析理论计算结果的合理性，研究不同中段开采充填情况下第四系底部的稳定性特征，最终得出安全开采所需的隔离层厚度必须在12m以上，合理的开采上限必须在-57m以上。通过分析数值计算模型第四系底部的沉降变形，发现第四系底部最大沉降集中于中间采场 ，最大沉降量为13.73mm。研究成果为滨海基岩矿床安全开采，提高资源回采率提供了有益指导。     

石墨烯改性涂层防护性能研究

为减少团聚，提高石墨烯在涂层中的分散性，研究采用纳米分散技术预先制备了石墨烯分散液，再将其分散至环氧树脂中获得石墨烯改性复合涂层。通过对石墨烯含量为 0、0.3%、0.6%的复合涂层进行盐水浸泡、盐雾、阴极剥离实验及电化学性能测试，证明石墨烯的加入显著增强了涂层的防护性能。石墨烯复合涂层在 3.5%盐水中浸泡 1 008 h后，涂层低频阻抗仍大于 106 Ω·cm²比未添加石墨烯的涂层提高了 3个数量级，且盐雾实验 6 000 h后涂层表面仍保持完好；含 0.6%石墨烯，的涂层耐蚀行为劣于石墨烯含量为 0.3%的涂层。     

Investigation on the anti-reduction mechanism of Ti4+ in high dielectric constant system Ca0.9La0.067TiO3 by doping with Al2O3

Ca_0.9La_0.067TiO₃ (abbreviated as CLT) ceramics doped with different amount of Al₂O₃ were prepared via the solid state reaction method. The anti-reduction mechanism of Ti⁴⁺ in CLT ceramics was carefully investigated. X-ray diffraction (XRD) was used to analyze the phase composition and lattice structure. Meanwhile, the Rietveld method was taken to calculate the lattice parameters. X-ray photoelectron spectroscopy (XPS) was employed to study the valence variation of Ti ions in CLT ceramics without and with Al₂O₃. The results showed that Al³⁺ substituted for Ti⁴⁺ to form solid solution and the solid solubility limit of Al³⁺ is near 1.11 mol%. Furthermore, the reduction of Ti⁴⁺ in CLT ceramics was restrained by acceptor doping process and the Q × f values of CLT ceramics were improved significantly. The CLT ceramic doped with 1.11 mol% Al₂O₃ exhibited good microwave dielectric properties: ε_r = 141, Q × f = 6848 GHz, τ_f = 576 ppm/°C.     

5CrNiMoV钢马氏体相变塑性和应力对其相变动力学的影响

利用DIL-805ADT动态相变膨胀仪测定了5CrNiMoV钢在低于奥氏体屈服强度的应力下的马氏体相变膨胀曲线,根据膨胀曲线分析并计算出了不同应力下Greenwood-Johnson相变塑性机制中的相变塑性系数k值和Koistinen-Marburger马氏体相变动力学模型中α和Ms的值,并且将Greenwood-Johnson模型和Leblond模型计算结果与实际试验值对比。结果显示:k值随应力的变化有所波动,但趋近于一个定值;通过对比,Leblond模型更符合试验结果;Ms点随着应力的增大呈现微小的上升趋势,说明小于或等于80 MPa 的应力对Ms点的影响不显著;拉应力下α值普遍大于无应力下的α值,压应力下α值普遍小于无应力下的α值,说明拉应力对相变有一定的促进作用,压应力对相变有一定的阻碍作用。     

汽车同步器齿环用耐高温结构胶膜的性能研究

同步器齿环与碳纤维耐摩擦材料是通过胶粘剂实现粘接,而胶粘剂耐高温性能的优劣则是决定其使用寿命的决定性因素。本文研究了环氧树脂E-51体系、环氧树脂AG80体系以及基材表面处理工艺对于结构胶膜耐高温性能的影响,采用熔融共混法制备了胶粘剂并以玻璃纤维布为背衬制备了耐高温结构胶膜。采用高低温拉力机对不同体系制备的结构胶膜进行了常温、200℃高温的钢材搭接剪切强度的测试。结果表明,对于E-51体系,提高体系交联密度可显著增大常温剪切强度,但高温剪切强度明显下降;对于四官能度的AG80体系,AG80的用量是影响其高温性能的主要因素,同时基材表面喷砂水洗处理后可显著增大结构胶膜与基材粘接有效面积,进而显著改善高温性能。所制备的结构胶膜较常用胶粘剂使用更加便捷,耐高温性能优良,满足同步器齿环使用要求。